tesa® 59650 can be tailored to meet specific application requirements with the following converting options:

Carrier material PET film
Type of adhesive type: tackified acrylic
Type of liner type: MOPP
Total thickness 160 µm
thickness of protective strip 80 µm
color transparent
color of security strip red
weight of security strip 72 g/m²

elongation at break 50%
tensile strength 20 N/cm
resistance to aging (uv) good
static shear resistance at 40°c very good
resistance to chemicals good
Temperature resistance, long-term 100 °C
initial adhesion good
static shear resistance at 23°c very good
Temperature resistance min. -40 °C
Temperature resistance, short-term 200 °C
moisture resistance very good
resistance to softeners good

Adhesion to ABS (initial) 9.8 N/cm
Adhesion to ABS (after 14 days) 10.8 N/cm
Adhesion to Aluminium (initial) 9.6 N/cm
Adhesion to Aluminium (after 14 days) 12.2 N/cm
Adhesion to PC (initial) 11.7 N/cm
Adhesion to PC (after 14 days) 13.1 N/cm
Adhesion to PE (initial) 5.2 N/cm
Adhesion to PE (after 14 days) 5.7 N/cm
Adhesion to PET (initial) 9.3 N/cm
Adhesion to PET (after 14 days) 10.5 N/cm
Adhesion to PP (initial) 5.3 N/cm
Adhesion to PP (after 14 days) 7 N/cm
Adhesion to PS (initial) 10.2 N/cm
Adhesion to PS (after 14 days) 11.1 N/cm
Adhesion to PVC (initial) 8.9 N/cm
Adhesion to PVC (after 14 days) 11.9 N/cm
Adhesion to Steel (initial) 11.3 N/cm
Adhesion to Steel (after 14 days) 13.4 N/cm